The TiO2 thin films were coated on the 100 meshes stainless steel 304 (SS304) sieves by using the sol-gel method followed by a thermal treatment at 200oC. The prepared TiO2-coated sieves were then employed to setup a photocatalytic reactor for evaluating their abilities on the degradation of VOCs (volatile organic compounds). The UV lamp was enveloped with a cylinder TiO2-coated sieve and located in the center of the reactor. A VOCs diffusing tube was applied to yield acetone under water bath. The yielded gaseous acetone was enforced to pass through the TiO2-coated sieves and reacted by photocatalytic reaction. Both the inflow gas and off-gas were monitored by a PID (photoionization detector) sensor for calculating the treat efficiencies under various conditions. The results showed that the amorphous structure was observed on the TiO2 films after sol-gel method, whereas the crystalline anatase phase was found after annealing at 200oC. The SEM images showed that the surface morphology of TiO2 coated SS304 sieves was very similar to that of uncoated sieves, demonstrating a good uniformity and thin thickness of the sol-gel coating method derived in this work. It was observed that most volatile acetone (almost 100%) was removed after treated with the designed photocatalytic reactor under a high fed flow rate (0.5- 2.0 l/min). As compared with the control experiments (UV OFF test), the adequate photocatalytic abilities of this developed TiO2 coated sieves were demonstrated. With the advantages of high contacting area with VOCs, low headloss, durable substrate and easy maintenance, the TiO2-coated sieves possessed a high potential for applying on the photocatalytic degradation of indoor air pollutants.
關聯:
Advanced Materials Research Volumes 123 - 125 P.919-922
如有問題歡迎與系統管理員聯繫 